Compound# L1001 92-avg.
durometer FEPM
|
Description: Formulated
AFLAS® Excellent ED resistance; Resistant to sour hydrocarbons |
Physical
Properties: |
|
ASTM
Method |
Property |
Avg. Value |
Min. Value |
|
D412 Method A |
Tensile Strength |
3330 psi |
2750 psi |
|
|
Ultimate Elongation |
115% |
80% |
|
|
Stress at Elongation |
|
|
|
|
- M25 |
1120 psi |
psi |
|
|
- M50 |
1660 psi |
1300 psi |
|
|
- M100 |
2805 psi |
2200 psi |
|
|
Strain Energy/ Unit Volume at 20% elongation |
127 psi |
|
|
|
Calculated Shear Modulus, G |
2381 psi |
|
|
|
Calculated Youngs Modulus, E |
7144 psi |
|
|
|
E-secant from the initial slope |
6715 psi |
|
|
D624, Die B |
Tear Strength |
288 psi |
|
|
|
|
Max Value |
Min Value |
|
D2240,
Type A |
Durometer Hardness |
95 points |
85 points |
|
D297,
15 |
Specific Gravity |
1.57 |
|
|
|
|
|
|
|
D395, Test B |
Compression Set |
Avg. Value |
|
|
|
22 hrs @ 392F |
23% |
|
|
|
70 hrs @ 392F |
33% |
|
|
|
336 hrs @ 392F |
46% |
|
|
|
Shelf Life |
20 years |
|
|
|
D865 |
Dry
Heat Aging |
|
|
|
|
Change in Tensile |
Change in Elongation |
Change in Durometer |
|
70 hrs @ 392F |
-6% |
-2% |
-3 points |
|
168 hrs @ 392F |
-4% |
25% |
0 points |
|
336 hrs @ 392F |
5% |
39% |
1 points |
|
1000 hrs @ 392F |
-1% |
43% |
-2 points |
|
|
|
Temperature Data |
|
|
D746 |
Brittle Point |
-40F |
|
D1329 |
Temp Retraction TR-10 |
36F |
|
|
Glass Transition |
37F |
|
|
Operating Temp |
425F |
Rev. |
6/26/1996 |
|
|
|
Meets specifications:
Halliburton ES-R-14-3, ES-R-12
Baker BPS-D202, AP900, C201
Dresser Rand 091-065
REDA MS-10-244
Halliburton 601.30000
Solar-Caterpillar ES 2028-1 AA |